Hind Crete Plus WPM
ACRYLIC POLYMER BASED CEMENTITIOUS COATING FOR WATER PROOFING
Hind Crete Plus WPM is an acrylic polymer based Cementitious coating and when used as recommended, combines with cement and fine sand to from an impermeable coating by blocking the capillaries and pores of the substrate of concrete. It is also UV resistant.
Technical Data Sheet (TDS)
Product Description
USES
Hind Crete Plus WPM is recommended for use in all structures that required to be waterproofed and protected against the ingress of moisture, like Roof / Terrace, Basements, Water tanks, Swimming pools, Retaining Walls, Bridge walls, Tunnels, Sewage tanks, Reservoirs, Dams, Dock Gates etc.
ADVANTAGES
- 1. Excellent adhesion to most building material.
- 2. Low permeability makes mortar or concrete waterproof.
- 3. Imparts chemical resistance to substrate.
- 4. Reduces or prevents salt penetration into concrete
- 5. Non toxic and can be used in water tank
APPLICATION
Substrate must be sound, clean free from loose particles or laitance and preferably wire brushed. The surface to receive the coating is to be checked first, if there are any cracks. If any cracks exist, it has to be repaired with cement mortar admixed with Hind Crete Plus WPM.. Undulation and depression to be filled and leveled to obtain even surface. The prepared surface must be thoroughly wetted with water and it has to be ensured that there is no standing water on the surface, before application of the coating.
COVERING CAPACITY
| Mix Information | Slurry Coat | Mortar | Repair |
| Hind Crete Plus WPM | 1 | 1 | 1 |
| Cement | 2 | 2 | 2 |
| Fine Sand | – | 2 | 3 |
| Consumption | 700 gm/Sq. Mtr. for two coats | 600 gm/ Ltr of mortar | 460 gm/ Ltr of mortar |
PROPERTIES
| Aspect | Milky White Liquid |
| Specific Gravity at 27ºC | 1.02± 0.01 |
| Corrosion Resistance (pH) | > 6 |
| Heat Resistance (ASTM C 1064-86) | Same as Concrete |
| Water Permeability (DIN: 1048 (P-5) | Nil |
| Tensile Strength (ASTM D 638) | 2 N/mm2 |
| Bond Strength | Concrete – 2N/mm2 + 0.2 |
| Metal – 2N/mm2 + 0.3 | |
| Service Life | Same as Concrete |
| Volatile Organic Content (VOC) | 51.4 gm/lit |
CURING
Over the coated surface, water is to be sprinkled after 6-10 hrs. Mild curing to be done after 24 hours of application. After 72 hours curing to be done vigorously and finally kept submerged in water for seven days.
Good results can be obtained if curing is carried on for further period of time.
SHELF LIFE
12 months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
PACKING
500 gm, 1, 5, and 20 kg in HDPE container or as required.
HANDLING PRECAUTION
Hind Crete Plus-WPM is non-toxic and prolonged skin contact should to be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice. Cleaning of tools is to be done with water.
Hind Crete Plus WPM (E)
HIGH PERFORMANCE ACRYLIC POLYMER BASED ELASTOMERIC WATERPROOFING COATING
Hind Crete Plus WPM (E) is a single component highly flexible, non toxic elastomeric waterproofing coating based on modified acrylic polymer.
Technical Data Sheet (TDS)
Product Description
USES
Hind Crete Plus WPM (E) is used for surface waterproofing of roofs, toilets, basements, swimming pools, water tanks etc. for providing a water impermeable membrane which is highly flexible and ultra violet resistant.
ADVANTAGES
- Highly flexible and thus has a crack bridging property.
- Resistant to ultra violet ray of sun.
- Non toxic and can be used for any kind of structures.
- Allows concrete to breath and enables any entrapped vapour to escape.
- Develops excellent bonding with building materials.
- It remains unaffected when applied within a wide range of temperatures.
- Unaffected when exposed to wide range of chemicals.
- Highly durable membrane and has a long functional life.
- Easy for recoating on existing surface coated with Hind Crete Plus
APPLICATION
Surface preparation
The surface should be cleaned from all loose materials, oil, grease, and washed properly. Any undulations, pot holes , wide cracks are to be properly mended with cement mortar and sufficiently cured. Before the application of Hind Crete Plus WPM (E) it is to be ensured that there is no stagnant water on the surface.
After the preparation of surface Hind Crete Plus WPM (E) is applied in three coats.
In the 1st coat Hind Crete Plus WPM ( E ) is mixed with clean water in the ratio 1 : 1 ( 1 part Hind Crete Plus WPM (E) : 1 part clean water ) and painted on the prepared surface with a flat paint brush @ 0.500 Kg / Sq. Mtr. of the diluted mixture.
When the 1st coat of diluted Hind Crete Plus WPM ( E ) is touch dry approximately after 4 hours of 1st coat, the 2nd coat of Hind Crete Plus WPM ( E ) is applied without any dilution on the surface with a paint brush @ 0.450 Kg / Sq. Mtr.
After a minimum time interval of 10 hours the third coat of Hind Crete Plus WPM ( E ) is applied without any dilution with a paint brush @ 0.250 Kg /Sq. Mtr.
CURING
A final air curing time of 48 hours is sufficient for complete curing of Hind Crete Plus WPM (E) .
COVERAGE
0.950 Kg /Sq. Mtr on a smooth surface in three coats for a Dry Film Thickness (DFT) of 0.5-0.6 mm .The coverage depend on the texture and porosity of the surface.
PROPERTIES
| Solid Content ( % age ) | 55- 57 |
| Aspect | Milky White Liquid |
| Specific Gravity | 1.2 |
| Corrosion Resistance (pH) | >6 |
| Hardness (Shore A) | 80 ( ASTM D 2240: 2002) |
| Tensile Strength (Mpa) | 2.8 ( ASTM D 412 :2002) |
| Elongation at break ( % ) | 600 ( ASTM D 412:2002) |
| UV Resistant (Accelerated) | Excellent, No failure (ASTM G 154 : 2000) |
| Weathering (1000 hours) | |
| Adhesion Strength , N/mm2 | 0.9 (ASTM D4541:2002 |
| Water Vapour Transmission | 19gm/m2 per day ( ASTM E 96:2000) |
| Resistance to Fungus & Algae | No Growth (SS 345:1998) |
| Crack Bridging | * No cracks up to 2mm width * No cracks up to 1mm (10 cycles) (ASTM C 836:1995) |
| Rapid Chloride Permeability | Negligible (Almost Nil) (ASTM C 1202-97) |
| Water Permeability (depth of penetration at 5 bar pressure) | 6 ( BS EN 12390, Part 8:2000) |
SHELF LIFE
12 months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
PACKING
5 Kg, 20 Kg in HDPE Containers
HANDLING PRECAUTIONS
Hind Crete Plus WPM (E) is non toxic, prolonged skin contact should be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice.
Note: The properties are based on laboratory conditions which may vary at site and in extreme weather conditions.
Hind Crete Plus WPM (E) RTU
TWO COMPONENT HIGHLY FLEXIBLE NON TOXIC ACRYLIC POLYMER BASED ELASTOMERIC WATERPROOFING COATING
Hind Crete Plus WPM (E) is a two component highly flexible, non toxic elastomeric waterproofing coating based on modified acrylic polymer.
Technical Data Sheet (TDS)
Product Description
USES
Hind Crete Plus WPM (E) RTU is used for surface waterproofing of roofs, toilets, basements, swimming pools, water tanks etc. for providing a water impermeable membrane which is highly flexible and ultra violet resistant. It is suitable for structures of all type even those in sea water/coastal environments.
ADVANTAGES
• Highly flexible and thus has a crack bridging property.
• Resistant to ultra violet ray of sun
• Non toxic and can be used for any kind of structures.
• Allows concrete to breath and enables any entrapped vapour to escape.
• Develops excellent bonding with building materials.
• Provides an excellent barrier coat against Carbon -dioxide, sulphate and chloride ions.
• It remains unaffected when applied within a wide range of temperatures.
• Unaffected when exposed to wide range of chemicals.
• Highly durable membrane and has a long functional life.
APPLICATION
Surface preparation
The surface should be cleaned from all loose materials, oil, grease, and washed properly. Any undulations, pot holes, wide cracks are to be properly mended with cement mortar and sufficiently cured. Before the application of Hind Crete Plus WPM (E) RTU it is to be ensured that there is no stagnant water on the surface.
Mixing
Component A (Liquid part) of Hind Crete Plus WPM (E) RTU is to be poured in a plastic bucket or metal container. Clean water as per the proportions shown in table below is to be added to it and mixed with a slow speed drill machine (500 rpm) fitted with a stirrer for a minute. Component B (Powder part) is now to be added gradually and mixed for 2-4 minutes. It has to be ensured that there is no lump formation while adding the powder part. After uniform mixing Hind Crete Plus WPM (E) RTU is to be applied immediately. It is advised not to mix more material at a time so that it can be used within the pot life of the mixed material. The mixed material must be stirred at intervals at the time of application to avoid settling down.
Ratio of Mixing
Hind Crete Plus WPM (E) RTU Components For Brush Application Pack Quantity
Component A (Liquid Part) 5 Kg
Component B (Powder Part) 15 Kg
Water 3 Ltr.
Application Procedure
The mixed material to be applied with a short stiff brushes over moist
or dampens surfaces. The substrate temperature at the time of
application should not be below 100 C. In hot conditions when the
temperature is more than 300 C, the substrate must be saturated with
water before the application. Two coats of Hind Crete Plus WPM (E) RTU
is recommended to achieve a 1 mm thickness of the coating. The second
coat is to be applied only after the first coat gets touch dried.
Surfaces/Area subject to heavy loads and Hydrostatic pressure 2mm
thickness coating is recommended for best results. In order to protect
the coating from getting damaged a screed cover is suggested. For better
bonding with the screed cover sand can be broadcasted over the second
coat when it is in green stage.
Drying Time
Within 4- 6 hours at normal temperature. Tools and equipments to be cleaned with water immediately after use otherwise mechanical cleaning are to be done.
COVERAGE
The coverage depends on the texture and porosity of the surface and also on the required consistency. The approximate coverage for (1 mm thickness) brush application consistency is 15-25 Sq Mtr/ 20 Kg Pack.
SHELF LIFE
6months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
PACKING
20 Kg Kit. Comp. A (Liquid Part) 5 Kg & Comp. B (Powder Part) 15 Kg
HANDLING PRECAUTIONS
Hind Crete Plus WPM (E) RTU is non toxic, prolonged skin contact should be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice.The properties are based on laboratory conditions which may vary at site and in extreme weather conditions.
Hind Styrene BR
POLYMER MODIFIED WATER RESISTANT REPAIR AND BONDING AGENT
Hind Styrene BR is a milky synthetic latex emulsion based on modified Styrene Butadiene Rubber (SBR) which imparts bonding, waterproofing and anti-weathering properties to cementitious systems.
Technical Data Sheet (TDS)
Product Description
USES
Hind Styrene BR has wide range of uses for waterproofing, as a grout admixture, in putties and in either forms, in the repair and rehabilitation industry, rendering and tile fixing etc and bonding old concrete to new concrete.
ADVANTAGES
- 1. Outstanding resistance to water and moisture.
- 2. Excellent adhesion to a wide range of substrates.
- 3. Improves flexibility of the treated area.
- 4. Improves mechanical properties and abrasion resistance.
- 5. Improves chemical resistance to substrates.
- 6. Low permeability makes mortars/concrete waterproof.
- 7. Improves workability and adhesion of mortars.
- 8. Strength remains unaffected.
- 9. Resists freeze-thaw phenomenon in cold climates.
- 10. Prevents finished surfaces from cracking.
- 11. Improves bond to mother substrates.
- 12. Weatherproofs walls from rising dampness/salt petre action.
APPLICATION
Surface preparation: The substrate must be structurally sound, clear and dust free, oil, grease and contaminants must be removed mechanically. Smooth surface must be scrubbed. Surface should be damped with water prior to application of the bonding primer, modified mortar or concrete. All excess water should be removed from the surface.
PROPERTIES
| Aspect | Milky White Liquid |
| pH | >6 |
| Specific Gravity | 1.02 ± 0.01 |
| Base | SBR (Styrene butadiene Rubber) |
Technical Informations
As tested in accordance with BS 6319 (wet cured) the values of the typical mechanical properties of 1:3 cement sand mortar at Water/Cement ratio -0.45 for control & Water/Cement Ratio -0.35 admixed with Hind Styrene BR (5Kg per 50 Kg cement) is given below:
| Mechanical Properties | Control Conditions | Hind Styrene BR |
| Compressive Strength N/mm2(BS 6319 Part-2 -1983) | ||
| 3days | 12.0 | 13 |
| 7days | 13.0 | 14.5 |
| 28 days | 22.0 | 23.5 |
| Tensile Strength N/mm2 at 28 days (ASTM C 190-85) | 2.5 | 3.5 |
| Flexural Strength N/mm2 at 28 days(BS 6319 Part-3 -1983) | 5.0 | 6.5 |
Note: Addition of increased dosages of Hind Styrene BR and further reduction of water leads to better and improved mechanical properties. Cementitiious based materials are less chemical resistant. Incorporation of Hind Styrene BR to cement mortars makes its impermeable and hence reduces the attack of aggressive chemicals.
APPLICATION & RECOMMENDED CONSUMPTION
| Ingredients | Bonding Coat /Waterproof coating | Polymer Mortar forPlastering | Polymer Concrete / Overlay |
| Cement | 3 to 3.5 partsby weight | 10 parts by weight | 10 parts by weight |
| Zone II Sand | Nil | 40 parts by weight | 15 parts by weight |
| 10 mm nominal size Coarse Aggregates | Nil | Nil | 30 parts by weight |
| Water | 1 part by weight | 4 parts by weight | 4 parts by weight |
| Hind Styrene BR | 1 part by weight | 1 part by weight | 1 part by weight |
| Hind Styrene BR :Water : Cement | 1:1 : 3 to 3.5 | 1:04:10 | 1:04:10 |
| Coverage | 0.250 to 0.50 Kg/m2/coat | 0.45 to 0.50 Kg/m2/10 mm thickness | 1 Kg/m2/ 25 mm thickness |
Note: For more economical designs the percentage weight of Hind Styrene BR with cement can be reduced keeping in view the requirements and uses. The various proportions as shown above are typical guidelines and may vary depending on site conditions, such as temperature, aggregate conditions, etc which leads to changing of W/C ratio for Polymer Mortar Plastering and polymer Concrete.
OTHER APPLICATIONS
| Mix proportion | Putty for joints | Sealant for tile joint |
| Hind Styrene-BR | 1 | 1 |
| Water | 1 | 2 |
| Cement (Grey) | 3.5 to 4 | — |
| Sand | 10.5 to 12 | — |
| White Cement | — | 4 to 4.5 |
| Lime stone powder | — | 4 to 4.5 |
| Color pigment | — | As required |
Polymer modified concrete (PMC) for construction joint or any other PMC. Mixed design specified as per site engineer. Hind Styrene BR 2 to 10% by weight of cement. Plasticiser cum water reducer may be used.
Polymer modified cement grout mix: Mix 4 to 8 % Hind Styrene BR by weight of cement with or without other grout admixture and 40 to 44% water for base plate and pocket grouting and for injection grouting.
SHELF LIFE
12 months from the date of manufacture in unopened conditions. To be stored in cool and dry place away from direct sunlight.
PACKING
500 gm, 1, 5, 20 Kg or as per requirement
HANDLING PRECAUTION
Hind Styrene BR is non-toxic, non-flammable and ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water and seek medical advice.
Hind Anti Rust
MODIFIED ACRYLIC POLYMER BASED ANTI CORROSIVE COATING
Hind Anti Rust is a modified acrylic polymer based cementitous, anticorrosive, protective coating.
Technical Data Sheet (TDS)
Product Description
USES
- 1. Anti corrosive and anti carbonation coating used for steel and concrete.
- 2. Coating to prevent corrosion for all types of reinforcement.
- 3. Corrosion protection for embedded corroded reinforcement at the time of repairing of damaged structure.
ADVANTAGES
- 1. Easy to use
- 2. Excellent bonding and adhesion to steel and concrete.
APPLICATION
Before application the substrate to be properly cleaned. Component A and Component B should be mixed in ratio of 1: 2. The first coat to be applied with a medium stiff brush. The second coat to be applied after 2-3 hours. On air curing for 2-3 hours after application of the second coat mortar, plaster or concrete may be done.
PROPERTIES
| Aspect | Comp. A- White bluish liquid, Comp. B- Grey powder |
| Pot Life | 30 mins. after mixing Comp. A and B |
| Bond Strength | 1.2 N/mm2 (approx). in case of steel2.0N/mm²(approx). in case of concrete |
| Coverage | 3 Kg. mixed material will give coverage of 4 Sq.mtr. on steel surface. |
SHELF LIFE
12 months from the date of manufacture in unopened condition. To be stored in a cool and dry place away from direct sunlight.
PACKING
1, 5 Kg.
HANDLING PRECAUTIONS
Hind Anti Rust is non-toxic and ingestion must be avoided. Any splashes on skin happens, immediately wash with water. If contacts with eyes occur, immediately wash with water and seek medical advice.
Hind ERS WS
WATER SOLUBLE EPOXY SEALER MEMBRANE
Hind ERS WS is a two-component system for waterproofing. The two parts are to be mixed thoroughly together and then diluted with water, before application
Technical Data Sheet (TDS)
Product Description
USES
To arrest seepage and dampness problems on interior surfaces of basements, tunnels, lift walls, retaining walls, floors, underground car parking etc. Being solvent free, it can be used on the interior of concrete water storage tanks. It is excellent on concrete that has hardened and is ideal as a waterproof membrane on concrete floor slabs under carpets and other floor coverings. It can be used as coating in breweries and food processing industries that follow FDA specifications.
ADVANTAGES
- 1. Useful in large areas of exposed concrete.
- 2. Can be applied on damp surfaces.
- 3. Dose not impair bond of subsequent adhesives or paints.
- 4. It possessed all the attributes of normal solvent based epoxy compositions, such as excellent water and fungal resistance, adhesion, hardness, mechanical strength and toughness to substrates.
- 5. Re coat ability and inter coat adhesive is excellent.
- 6. Easily washable with a soap solution.
- 7. May be tinted with universal paint tinters.
- 8. Being free of solvent, it does not pose any health hazards or fire hazards.
- 9. Waterproofing work can be executed even during the monsoon on wet substrates.
- 10. It is completely safe, convenient and economical to apply.
APPLICATION
Before application, surface preparation is important. Surface should be clean, free from loose particles, oil, grease, or other foreign materials. Deep contaminated concrete should be thoroughly cleaned by wire brush, or sand blasted.
No primer is required before the application of Hind ERS- WS. Apply two coats using a stiff nylon brush or roller. Allow 3 to 4 hours gap between first and second coat.
PROPERTIES
| Aspect | Off white in color of mixed material. |
| Mixing Ratio | Component A: Component B: Water = 1:1:1 (by weight). Stir individual components thoroughly before mixing together. Then mix both components and dilute the mixed compound with water by slow addition, using a low speed mixer |
| Pot Life | 60 to 70 minutes at 30ºC |
| Drying Time | 4 to 6 hours. |
| Curing Time | 24 hours. |
| Coverage (Mixed) | First coat- 6 to 9 Sq.mtr / Kg. Second coat – 8 to 10 Sq.mtr / Kg. |
| Film Appearance | Semi Glossy smooth film. |
| Hardness, Toughness | Excellent |
| Water Resistance | Excellent |
| Adhesion to controlled damp surface | Good |
| Impact Resistance | Good |
| Chemical Resistance | Good |
SHELF LIFE
12 months from the date of manufacture in unopened condition.
PACKING
1, 2, 5 Kg or as per requirement
HANDLING PRECAUTION:
Hind ERS – WS is non-toxic, non-flammable and ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water.
Hind Hydro Proof
APP MODIFIED ELASTO-POLYMERIC MEMBRANE WATERPROOFING SYSTEM
Hind Hydro Proof range of waterproofing membranes are an elasto-plastomeric (APP- Atectic Poly Propylene) modified bitumen membrane having a dimensionally stable non-woven polyester / fiberglass carrier to obtain excellent waterproofing, heat resistant & cold temperature flexibility, high tensile strength, tear, puncture & UV resistance.
Technical Data Sheet (TDS)
Product Description
USES
- Waterproofing of flat roof surfaces.
- Waterproofing of slant roof.
- Waterproofing of tunnels.
- Waterproofing of roof gardens.
- Waterproofing of swimming pools.
TECHNICAL DATA
| Product Name | Hind Hydro Proof (1 mm) | Hind Hydro Proof (P 160) | Hind Hydro Proof (P 180) | Hind Hydro Proof (P 160) W/Minerals | Hind Hydro Proof (FG 050) | Test Method |
| Roll size, mtrs. Thickness, mm Carrier Weight | 20 x 1 1 mm 120 g/m2 Non- Woven Polyester | 10 x 1 2,3 & 4 160g/m2 Polyester | 10 x 1 2,3 & 4 180g/m2 Polyester | 10 x 1 2,3 & 4 180g/m2 Polyester | 10 x 1 2,3 & 4 50g/m2 Polyester | ASTM D 146 ASTM D 146 |
| Coating Asphalt | APP modified | APP modified | APP modified | APP modified | APP modified | ASTM D 36 |
| Softening Point [R&B] 0C | 120 to 125 | 150 | 150 | 150 | 150 | X |
| Penetration at 250C, dmm | 15 – 25 | 15 – 25 | 15 – 25 | 15 – 25 | 15 – 25 | ASTM D 5 |
| Tensile Strength [L/T] N/5cm | 500/400 | 700/550 | 800/660 | 700/550 | 300/200 | ASTM D 882 |
| Elongation at break [L/T] % | 40/40 | 40/50 | 40/50 | 40/50 | 2/3 | ASTM D 882 |
| Cold Flexibility 0C | 00 C | 0 to – 5 | 0 to – 5 | 0 to -5 | 0 to -5 | ASTM D 4586 |
| Lap Joint Strength [L/T] N/5cm | X | >700/550 | >800/660 | >700/550 | >300/200 | ASTM D 882 |
| Tear Resistance[L/T] N | 100/110 | 150/170 | 180/200 | 150/170 | 55/70 | ASTM D 4073 |
| Resistance to water pressure | No Leakage | No Leakage | No Leakage | No Leakage | No Leakage | ASTM G 53 |
| Water Absorption [%] | <0.15 | <0.15 | <0.15 | <0.15 | <0.15 | ASTM D 5147 |
| Heat Resistance At 1000C | No Flow | No Flow | No Flow | No Flow | No Flow | ASTM D 4586 |
| Resistance to ageing After 2000hrs. | No deterioration | No deterioration | No deterioration | No deterioration | No deterioration | ASTM D 4799 |
5-20% variation under tolerance limit as per ASTM standards
ADVANTAGES
· 100% water impermeable membrane.
· Very easy application.
· Over lay is possible with desired finish.
· Application is very fast and time saving.
APPLICATION PROCEDURE
Hind Hydro Proof is installed by torch bonding using a suitable gas torch. The substrate should be cleaned and primed with Hydro prime i.e. Bituminous Primer and allowed to dry. Then the Hind Hydro Proof is torched at the bottom while unrolling. The torching to be controlled to ensure only the PE film is melted and the asphalt coating is sufficiently softened to bond the membrane. The torch flame should be directed between the lower part of the roll and the substrate. Overlaps of 75 to 100 mm for side laps and 100 to 150 mm for end laps must be torched. All angles and abutments should be sealed with extra care to ensure full bondage. Seal the edges in to grooves and protect with suitable sealant.
SHELF LIFE
24 months from the date of manufacture. To stored in a cool and dry covered place away from direct sunlight.
PACKING
In rolls of 10 Metre Length
Hind Marine Cote
ANTI- CORROSIVE COATING BASED ON ACRYLIC POLYMER FOR ALL ENVIORNMENT
Hind Marine Cote is a single component cement based polymer modified coating formulated to protect the corrosion of all types of steel and concrete surface especially influenced by seawater and severe saline environment. To use it as a coating against corrosion, it should be used in conjunction with Cement.
Technical Data Sheet (TDS)
Product Description
USES
Hind Marine Cote is recommended for use as a corrosion protective coating for all types of steel structure and steel reinforcement used in concrete and concrete surface under severe conditions especially saline environment, sea and fresh water conditions. It can also be used for corrosion protection of bridge & ship decks, sheet pilling surge shaft, other dam structures in severe conditions and for water tanks and sub grade water pipes.
ADVANTAGES
- 1. Easy to use and has excellent adhesion to steel and concrete.
- 2. Not affected by the influence of ultra violet rays.
- 3. Excellent bonding properties and can be applied in moist & wet conditions.
- 4. Absolute and improved adhesion to reinforcements.
- 5. Non-toxic, Non-flammable and is not harmful to human health.
- 6. Not affected by chemicals in the range of mild acids to strong bases.
APPLICATION
Surface preparation is one of the vital steps before application of any coating. The surface should be made dry, free from oil or grease and made clean from all loose scale. The polymer is to be mixed with Cement in the ratio of 1: 2 by means of hand drill until a uniform colored paint able consistency is got. It can be applied by hand rollers, brush or spray. It is always recommended to apply two coats and the interval between the two coats will be of 2-3 hrs, until the first coat is completely dried up. Adequate curing by sprinkling water to be done to get best results. In continuous water exposure conditions a minimum curing for 72 hours is recommended.
PROPERTIES
| Aspect | Milky White Liquid |
| Coverage | 3.5-4.0 Sq. Mtr per Kg. (Mixed Condition) for 2 coats. |
| Mix Proportion | Hind Marine Cote –1Part : Cement -2 Parts |
| Density at 27 0 C | Approx. 1.01Kg/Ltr. |
| Mixed Density | Approx. 2.12 Kg/Ltr. |
| Pot Life at 27 0 C | 20-25 minutes. |
SHELF LIFE
12 months from the date of manufacture in unopened container. To be stored under shed and away from direct sunlight.
PACKING
5, 20 Kg in HDPE Containers
HANDLING PRECAUTION
Hind Marine Cote is non-toxic but ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water and seek medical advice.
Hind Hydraproof Ceramic
INSULATIVE AND WATERPROOFING COATING FOR MASONRY, METAL, TIMBER AND FIBER APPLICATIONS
Hind Hydraproof Ceramic is an emulsion of high grade Ceramic Polymer in water. It contains the added advantages of ceramic particles which are the heat and cold dissipating elements that give the ability to save on heating and cooling costs. It dries by evaporation to yield a tough, velvety, non-yellowing, watertight surface with highly abrasion resistance and Ultraviolet stability. Hind Hydraproof Ceramic when applied directly to rust will prevent further rusting problem.
Technical Data Sheet (TDS)
Product Description
USES
Hind Hydraproof Ceramic is used to provide a coating to insulate most building materials from solar heat. Hind Hydraproof Ceramic does not require a primer in most cases due to the unique properties of the material.
ADVANTAGES
- Energy Saving
- Cost Saving and Efficient
- Water tight Membrane
- Maintain an Attractive Appearance
- Non Toxic, Non Flammable
- Built-in rust Inhibitor
- Prevent Rust
- Non-Yellowing
- Excellent adhesion, no primer required in most cases
- High UV resistance
- Water based, Single pot material
- Quick drying
- High Solar Reflectivity
- Temperature Reduction
- Highly Flexible
- Corrosion and Abrasion Resistance
- Fungal Resistance
APPLICATION
Brush or Roller
Pre wet the brushes and rollers to avoid clogging. Apply two coats straight from the container. Allow two hours between conventional spray.
Airless Spray
Thin with up to 10% clean water to aid atomization. Use a tip orifice of 0.5 micrometers or larger. Apply the material in two even coats. Allow two hours between coats. Do not apply if temperature is or will fall below 100C or high humidity, rain or dew as Hind Hydraproof Ceramic will not cure properly. If the conditions are hot or windy, and it is necessary to coat in these conditions the surface should be cooled using water hose. Hind Hydraproof Ceramic can be applied over the damp cool surface. If Hind Hydraproof Ceramic is not dry within one hour, cease coating immediately. Where the application is used for the collection of drinking water, down pipes should be kept open until the area has had two or three rinses with rain water. Surface must be cleaned, dried and free of any oil, grease or dirt by approved method prior to application of Hind Hydraproof.
Ceramic
Two coats are recommended for dry film of not less than 300 microns (0.3 mm). Allow two hours to dry before apply second coat.
MIXING
Mix thoroughly with a flat stirrer or mechanical mixer before using. Hind Hydraproof Ceramic dose not normally need to be thinned but if considered necessary, 10% of clean water may be added.
COVERAGE
| Theoretical coverage | 4.0 Sq. Mtr/Kg/Coat |
| Recommended Coats | 2 Coats |
PROPERTIES
| Color | White / Cream / Grey |
| Coating Type | Ceramic Coating |
| Cleaning | Water |
| Flash Point | None |
| Solid by Volume | 60% |
| Film Thickness | 300 micron (Minimum) |
| Drying Time | 30 minutes / 250C |
| Recoating Time | 2 hours |
| Min. Application Temperature | 100C |
| Max. Application Temperature | 350C |
| THERMAL PROPERTIES |
| Solar Reflectance 93% Solar Absorbance 7% Thermal Emission 92% Transmittance 0% Define as opaque material |
| PHYSICAL PROPERTIES |
| Surface Adhesion >15 ksc (ASTM C-633) Flexibility No cracking breakage Elongation -500% (ASTM D-412) Fungal Resistance No fungal growth Water Transmission No water transmit Vapour Transmission 0.1 perms (ASTM E-96) Chemical Resistance No corrosion Maximum Service 1200C Temperature No cracking breakage Fire Resistance (ASTM E-84) Flame spread 5Fuel contribution 0 Smoke density 0 |
SHELF LIFE
12 months from the date of manufacture in unopened condition. To be stored in a cool and dry place away from direct sunlight.
PACKING
1, 4, 20, 200 Kg in HDPE Container.
HANDLING PRECAUTION
Hind Hydraproof Ceramic is non-toxic non-flammable and ingestion is to be avoided. Any splashes to the skin must be washed with water. If contact with eyes occurs, wash well immediately with water and seek medical advice.
Hind Wall Putty
VERSATILE WATER RESISTANT WHITE CEMENT BASED WALL PUTTY
Technical Data Sheet (TDS)
Product Description
USES
Hind Wall Putty is used on the interior and exterior wall surface and ceiling, to protect the base from water absorption, hence making the base 100% waterproof before application paint. It improves the adhesion with concrete and a smooth surface is obtained for paint with higher coverage rate.
ADVANTAGES
• Provides an excellent bond with concrete walls, being a cementitious base material.
• Eco-friendly& Non-toxic. It does not contain lead or any harmful chemicals.
• Water curing is not required after application, hence it is cost effective.
• No primer is required to be applied on it before application of paint resulting to cost saving.
• Ensures a smooth finished surface with less consumption of paints.
• Cab be applied on both exterior & interior walls & ceiling.
• All types of paints can be applied on it.
• Growth of Algae & fungi are prevented on the wall.
• Can be applied on old used surface after proper surface preparation.
• Can be applied over moist surface.
APPLICATION
Surface Preparation
Before application surface preparation is very important. Surface should be clean, free from loose particles, oil, grease or any other foreign materials. The substrate should be thoroughly cleaned by sand paper or wire brush.
Mixing
Add 50% water to Hind Wall Putty and mix with a mechanical mixer for 10-15 minutes to obtain an uniform paste. We recommend using a mechanical mixer to get better coverage. It is very essential and has to be ensured that water is added to Hind Wall Putty and not vice-versa. It is advised to mix required quantity of the material , so that it can be consumed within 2-3 hours of mixing water.
Preparation of Substrates before application
Before application of Hind Wall Putty the surface to be thoroughly pre-wetted and application done on wet surface to ensure effective adhesion, workability and more coverage on the surface.
After application of the 1St coat, the surface is allowed to dry for 3 hours and then the 2nd coat of putty is applied and made to dry completely for 10-12 hours. The total thickness of coats is to be limited to a maximum of 1.5 mm. Before application of paint/distemper it is to be assured that the surface is even and smooth. This is achieved by rubbing the putty applied surface with 500 No. sand paper. We recommend 2 (Two) coats of putty application to be done before applying paint.
PROPERTIES
Aspect White Powder
Compressive Strength at 270C at 28 days >9.0 N/mm2 as per EN:196
Tensile Adhesion Strength at 270C at 28 days >1.0 N/mm2 as per EN:1348
Setting Time Initial > 100
Final < 490 As per EN : 196
Water Absorption Co-efficient (kg/m2,H1/2) < 1.0 as per DIN:52617 Water Retentivity (%) >99 as per EN:196
Water Capillary Absorption in 24 Hrs (ml) 0.88 as per Karsten Tube Test
COVERAGE
2-3 Sq. Mtr/Kg/mm is achieved in 2 (two) coats on smooth and normal surface. However, cover area depends on the quality of the substrate.
SHELF LIFE
6 months from the date of manufacturing. Should be stored in a cool and dry place away from direct sunlight.
PACKING
Available in 20Kg. polylined HDPE Bag or as required.
HANDLING PRECAUTION
Hind Wall Putty is non-toxic but ingestion is to avoided. If contact with eyes occurs, wash well immediately with water and seek medical advice.
Note:
• Hindcon Chemicals maintains a team of technically trained professionals to provide full support to your problems in construction, and recommend the correct product to suite your specific requirements. Our authorized applicators can attend your site for application of the products.
• The content of the Technical datasheet are for general information and guideline. The result shown here are generated from our laboratory or from our site experiences.
• Quality of our products are maintained as per ISO9001:2008 recommendations and continuous researches. The behavior can change as per the prevailing conditions at the time of applications.
• Since HINDCON CHEMICALS LIMITED has no control over the use to which the users may put the material, it does not claim or warrant that in the user’s particular circumstances, the result that the user will obtain from the product will be the same as those described in this communication or that the user will find the information or recommendations complete, accurate or useful. The client must test and ascertain the safety and fitness for the product for use.
Hind Plasto Guard
ALL PURPOSE ACRYLIC POLYMER BASED WATERPROOFING AND PROTECTIVE COATING
Hind Plasto Guard is a single component, flexible, ultra violet and weather resistant waterproofing coating based on modified acrylic polymer. It also possesses the property to reflect the heat from the applied surface which results in producing a cooling effect. It can be applied to all exposed flat, sloped and vertical concrete, masonry and metal surfaces.
Technical Data Sheet (TDS)
Product Description
USES
Hind Plasto Guard is used for surface waterproofing and weather resistant coating for concrete flat, sloped roofs, parapet walls, basements, swimming pool, water bodies, RCC/Lime terraces/Asbestos , sunken portion of Toilets & Kitchen, Chajjas and on the exterior surface of PVC/Metal water tanks placed on roofs/balconies which allows to keep the temperature of the water inside the tank cooler to some extent.
ADVANTAGES
- Single Component hence easy to use
- Highly flexible and thus has a crack bridging property
- Easy and fast application with economical cost
- Resistant to ultra violet ray of sun
- Non toxic and can be used for any kind of structures
- Allows concrete to breath and enables any entrapped vapour to escape
- Develops excellent bonding with building materials
- It remains unaffected when applied within a wide range of temperatures
- Unaffected when exposed to wide range of chemicals
- Highly durable membrane and has a long functional life
- Does not allow fungal growth due to weathering action
- Environment friendly with a high diffusion resistance against CO2
- Water based
- No protection screed is required under normal foot traffic condition.
- Against high wear & tear condition if expected it requires to be protected with a protective screed.
APPLICATION
Surface preparation
The surface should be cleaned from all loose materials, oil, grease, and washed properly. Any undulations, pot holes , wide cracks are to be properly mended with cement mortar and sufficiently cured. Before the application of Hind Plasto Guard it is to be ensured that there is no stagnant water on the surface.
After the preparation of surface Hind Plasto Guard to be applied as first coat @ 0. 2Kg/m2 . For best result two coats are recommended.
Hind Plasto Guard can be applied along with Hind Fiber Glass, which is to be embedded between the first and second coat @ 0.7 to 1.0 Kg/m2 per coat, depending on the porosity of the surface in green condition. When the second coat gets cured and become touch dry, a top coat (~ 0.3 Kg/m2 ) is applied to complete the application. The coated surface to be protected from rain until is gets completely dry.
COVERAGE
Without using Fibre Glass : 0.4 to 0.5 Kg/m2 for two Coats whichdepends on the surface porosity.
Using Fibre Glass : 2 -2.5 Kg/m2 which depends on the surface porosity.
Thickness of Coating without Hind Fiber Glass is 1.0 mm and with Hind Fiber Glass is 1.2 mm approx.
PROPERTIES
| Aspect | Acrylic Dispersion, White/ Grey and various other colours |
| Solid Content | 65% |
| Polymer Content | 34.40% |
| Sp. Gravity at 270 C | 1.14 + 0.02 |
| Bond Strength ISO 4624 | 1.5 N/mm2 |
| Salt Spray resistance | Good |
| Water Permeability (IS 2645) | Passes |
| Moisture Permeability (IS 101) | Passes |
| Crack Bridging (ASTM C 1305-06) | 2mm |
| Crack Resistance (IS101) | Passes the 3 mandrel |
| Workable Time | 15 to 20 mins at 270 C |
| Tack Free | 25 -30 mins at 270 C |
| Drying Time | 2-3 hours depending upon the ambient temperature |
| Application Temperature | 100 C to +350 C |
| Accelerated Weathering test 500 hours (IS 101) | No Cracking /Blistering |
SHELF LIFE
12 months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
PACKING
1Kg, 5 Kg, 20 Kg & 50 Kg in HDPE Containers
HANDLING PRECAUTIONS
Hind Plasto Guard is non toxic, prolonged skin contact should be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice.
Note: The properties are based on laboratory conditions which may vary at site and in extreme weather conditions.
Hind Hydrolast 2K
ACRYLIC POLYMER BASED CEMENTITIOUS COATING FOR WATER PROOFING.
Hind Hydrolast 2K is a two component, elastomeric, flexible, acrylic polymer modified cementitious coating and when used as recommended, it forms an impermeable coating by sealing the capillaries and pores of the substrate of concrete. The flexible property of the product enables it to overcome thermal stress, expansion and contraction of the structures due to changes in weather. It conforms to IS: 6582 & ASTM D 2370.
Technical Data Sheet (TDS)
Product Description
USES
Hind Hydrolast 2K is recommended for use in all structures that required to be waterproofed and protected against the ingress of moisture, like Roof / Terrace, Basements, Water tanks, Swimming pools, Retaining Walls, Bridge walls, Tunnels, Sewage tanks, Reservoirs, Dams, Dock Gates etc. It can be reinforced with Hind Fiber Glass to enhance the dimensional stability of the structure.
ADVANTAGES
- Excellent adhesion to most building material.
- Low permeability hence protects concrete from water penetration, chloride and carbonation.
- Imparts chemical resistance to substrate.
- Reduces or prevents salt penetration into concrete
- Non toxic and can be used in water tank.
- Easy to apply by brush or spraying.
- Ready to use, addition of water not recommended.
- Flexible and Crack bridging.
Application
Before application the substrate must be sound, clean free from loose particles or laitance and preferably wire brushed. The surface to receive the coating is to be checked. If any cracks exist, it has to be repaired with trowel able mortar of Hind Hydrolast 2K. Undulation and depression to be filled and leveled to obtain even surface. The prepared surface must be thoroughly wetted with water and it has to be ensured that there is no standing water on the surface, before application of the coating. On the dampen surface for slurry consistency first coat of Hind Hydrolast 2K to be applied by brush or sprayed. On drying of the first coat after an interval of 4-5 hours second coat to be applied depending on the temperature and humidity. Addition of water to the prepared slurry of Hind Hydrolast 2K is not at all advised. It is recommended to apply two coats for waterproofing and damp proofing with layer thickness ranging between 1.5mm to 2.0 mm. For areas where there is severe leakages a third coat is recommended. For trowel able mortars use of notched trowel is to be done. The coated surface is not trafficable and needs to be protected with screed concrete mixed with Hind Styrene BR (SBR Latex) to prevent it from getting damaged.
Curing
It is very much essential, that cementitious based coating is cured properly for 3-4 days for ensuring proper hydration of cement and preventing from cracking. If possible we recommend curing for 7 days by water logging over the surface or keeping it covered with dampen used jute to obtain better result of the coating.
PROPERTIES
| Aspect | Pack A :Milky White Liquid Pack B : Grey Powder Mixed Material : Cement Grey |
| Mixing Ratio | Pack A : Pack B :: 1 :3 (By weight) |
| Density | ~ 2.00Kg/Ltr. at 27 + 20 C |
| Corrosion Resistance (pH) | >6 |
| Elongation at Break | ~ 8-10% with Hind Fibre Glass |
| Compressive Strength at 27 + 20 C | ~ 2 N/mm2 in 3 days ~ 20 N/mm2 in 28 days |
| Pot Life | 30-40 minutes at 270 C |
| Coverage | ~ 1.5 Kg /m2 in two coats (First Coat) ~ 1.0 Kg/ Sq.Mtr (Hind Fibre Glass) ~ 1.5 Kg /m2 in two coats (Top Coat) Coverage is depending on the porosity and texture of the surface. |
| Thickness of Layer | 1.5 – 2mm average thickness with Hind Fibre Glass. |
| Application Temperature | Substrate – 100 C (Min) /400 C (Max.) Ambient Temperature – 100 C (Min) /400 C (Max.) |
| Heat Resistance (ASTM C 1064-86) | Same as Concrete |
| Pull Out Bond Strength | Concrete – 2 N/mm2 + 0.2 (Concrete Failure) as per ISO 4624 Metal – 2 N/mm2 + 0.3 as per ISO 4624 |
| Tensile Strength (ASTM D 638) | 2 N/mm2 after 14 days in exposed condition |
| Water Penetration (DIN: 1048 (P-5) | Nil |
| Service Life | Same as Concrete |
SHELF LIFE
12 months from the date of manufacture in unopened condition. Should be stored in a cool and dry place away from direct sunlight.
PACKING
20 Kg Kit.
HANDLING PRECAUTION
Hind Hydrolast 2K is non-toxic and prolonged skin contact should to be avoided. In case of contact with eyes occurs wash with plenty of clean water and seek medical advice. Cleaning of tools is to be done with water.
Hind Hydroflex Polyurea (H)
TWO COMPONENT, CHEMICAL RESISTANT, RAPID CURING POLYUREA BASED WATERPROOFING MEMBRANE
Hind Hydroflex Polyurea (H) is two component, chemical resistant, rapid curing polyurea based waterproofing membrane. It contains 100% solid, pre-heated and spray applied rapid curing elastomeric waterproofing membrane and has excellent resistant to wide range of common chemicals.
Technical Data Sheet (TDS)
Product Description
USES
Hind Hydroflex Polyurea (H) is recommended as a waterproofing and protective coating for structures that are exposed to wide range of aggressive chemical and environmental conditions. Typical applications include Potable Water tanks, Water Retaining structures, Underground Structures, Foundation walls and sumps, and Bridge Deck waterproofing etc.
ADVANTAGES
- 1. It is Moisture Insensitive and Rapid
- 2. It forms seamless membrane.
- 3. UV Resistant.
- 4. Zero VOC and is Eco-friendly.
- 5. Excellent Abrasion, Impact and Puncture resistant.
- 6. Posses an excellent chemical resistant property.
- 7. Can be applied in wide range of extreme weather conditions ( – 50 0 C to 200 0 C )
- 8. Is available in wide range of attractive colours.
SURFACE PREPARATION
Suitable surface preparation to be should done by water jetting or wet grit blasting to make the surface free from oil, grease, all loose particles, laitance and other foreign containments. Undulation, honey combs, voids and blow holes are to be rendered smooth with Hind Polymer mortars. If fine cracks are identified, it is to be grouted with Hind ERS 21/Hind ERS 21 (LV) epoxy resin system. Application to be done only on dry surface.
APPLICATION
Prior to application of Hind Hydroflex Polyurea (H), it is recommended that the surface to be primed with Hind PU Primer @ 0.2-0.3 Kg/m2. It is always advisable that proper high pressure spray pump (GRACO make) is used for application of Hind Hydroflex Polyurea (H) as per the following guidelines:
| Output Pressure | Up to 2000 psi |
| Minimum Spray Pressure | 1600 – 1800 psi |
| Temperature Setting | 60 0 C |
| Hose Temperature | 50 0 C – 550 C |
PROPERTIES
| Solid Content | 100% |
| Density at 250 C | 1.1- 1.2 Kg / Ltr |
| Mix Ratio (By volume) | 1: 1 |
| Viscosity at 250 C | 400-1000 cps |
| Tensile Strength | 19 Mpa |
| Elongation | > 400% |
| Tear Strength N/mm | 55 |
| Hardness (Shore A) | 85-95 |
| Tack free time (T.F.T) | 5-15 seconds |
| Trafficable (Light) | 3-5 minutes |
| Fully Serviceable | 12 hours |
THICKNESS
Minimum dry film thickness of 1.5 mm is achieved @ 1.8 Kg/m2.. The thickness of the membrane may vary depending on the application process.
PACKING
Available Pack A in 210 Kg & Pack B in 200 Kg Container.
STORAGE
12 months in original unopened container. Do not expose or open container to high humidity conditions.
HANDLING PRECAUTION
Hind Hydroflex Polyurea (H) is non-toxic. Wearing of Hand gloves, mask, shoes and Safety goggles is a must while using and handling the product.
Hind Hydroflex Polyurea (P)
TWO COMPONENT, CHEMICAL RESISTANT, RAPID CURING PURE POLYUREA BASED WATERPROOFING MEMBRANE
Hind Hydroflex Polyurea (P) is two component, chemical resistant, rapid curing pure polyurea based waterproofing membrane. It is solvent free and MDI as an Isocyanate is added which has low vapour pressure. This system functions with the Polyamine and Amine chain extender as a resin part and does not react with Polyol resulting to fast curing with the presence of any Catalyst. It can be used as an internal coating for potable water concrete tank which is safe for human consumption. The gel time of the system ranges from 5-15 seconds and curing time of 3-5 minutes. It contains 100% solid, pre-heated and spray applied rapid curing elastomeric waterproofing membrane and has excellent resistant to wide range of aggressive chemicals.
Technical Data Sheet (TDS)
Product Description
USES
Hind Hydroflex Polyurea (P) is recommended as a waterproofing and protective coating for concrete and steel substrate that are exposed to wide range of aggressive chemical and environmental conditions. Typical applications include Potable Water tanks, Pipe coating (concrete, steel), Underground Structures, Foundation walls and sumps. Submerged Structures, Concrete and Steel surfaces in sewage treatment plant, Marine Structures requiring protection, Chemical Plants, Crude oil storage tanks, Paper Mills, Dams, Barrage gates, Penstocks, Iindustrial effluent treatment tanks and Bridge Deck waterproofing etc.
ADVANTAGES
- 1. It is Moisture Insensitive and Rapid
- 2. It forms seamless membrane.
- 3. Zero VOC and is Eco-friendly.
- 4. Excellent Abrasion, Impact and Puncture resistant.
- 5. Posses an excellent chemical resistant property.
- 6. Can be applied in wide range of extreme weather conditions ( -50 0 C to 200 0 C )
- 7. Is available in wide range of attractive colours.
SURFACE PREPARATION
Suitable surface preparation to be should done by water jetting or wet grit blasting to make the surface free from oil, grease, all loose particles, laitance and other foreign containments. Undulation, honey combs, voids and blow holes are to be rendered smooth with Hind Polymer mortars. If fine cracks are identified, it is to be grouted with Hind ERS 21/Hind ERS 21 (LV) epoxy resin system. Application to be done only on dry surface.
APPLICATION
Prior to application of Hind Hydroflex Polyurea (P), it is recommended that the surface to be primed with Hind PU Primer @ 0.2-0.3 Kg/m2. It is always advisable that proper high pressure spray pump (GRACO make) is used for application of Hind Hydroflex Polyurea (P) as per the following guidelines:
| Output Pressure | Up to 3500 psi |
| Minimum Spray Pressure | 1800 – 2500 psi |
| Temperature Setting | 60 0 C – 700 C |
| Hose Temperature | 60 0 C – 700 C |
PROPERTIES
| Solid Content | 100% |
| Density at 250 C | 1.1- 1.2 Kg / Ltr |
| Mix Ratio (By volume) | 1: 1 |
| Viscosity at 250 C | 300-1500 cps |
| Tensile Strength | 20 Mpa |
| Elongation | > 300% |
| Tear Strength N/mm | 90 |
| Hardness (Shore A) | 90-100 |
| Tack free time (T.F.T) | 5-15 seconds |
| Trafficable (Light) | 3-5 minutes |
| Fully Serviceable | 12 hours |
THICKNESS
Minimum dry film thickness of 1.5 mm is achieved @ 1.8 Kg/m2.. We recommend 2 mm thickness for waterproofing and chemical resistance and 3mm thickness for heavy duty abrasion resistance.
PACKING
Available Pack A in 210 Kg & Pack B in 200 Kg Container.
STORAGE
12 months in original unopened container. Do not expose or open container to high humidity conditions.
HANDLING PRECAUTION
Hind Hydroflex Polyurea (P) is non-toxic. Wearing of Hand gloves, mask, shoes and Safety goggles is a must while using and handling the product.
Hind Seal Cote
SODIUM SILICATE BASED INTERIOR/ EXTERIOR SURFACE WATERPROOFING COATING
Hind Seal Cote is an unique Sodium Silicate based coating and can be applied to exterior & interior wall & roof surface by brush/spray application to achieve waterproofed surface. It is a colourless and ready -to-use compound containing active chemicals which penetrates deep into the surface. On application of Hind Seal Cote, the exterior plastered and concrete surface gets hardened and becomes waterproofed and chemical resistant. It reacts with the cement chemically and penetrates deeply to solidify all ingredients in the plaster and concrete to form a homogenous mass. The solidification leads to hardened surface, hence surface cracks and spalling is restricted.
Technical Data Sheet (TDS)
Product Description
USES
On its application an improved highly chemical resistant surface is obtained. It is used for all type of industrial exterior/interior wall, roof waterproofing application in residential buildings, warehouses, chemical processing plants, and interior/exterior walls of storage silos, refineries, airport, hospitals and museums.
ADVANTAGES
- It provides a tough abrasion resistant surface which does not turn yellow or decolourizes .
- Single component, ready to use.
- It penetrates deep into the surface, densify and hardens the plastered and concrete surface which does not allow entry of moisture or any other foreign matter
- Scratch and peel proof.
- Chemical resistant and surface becomes abrasion resistant .on its application.
- It is cost effective due to high coverage.
- Surface becomes crack resistant on its application.
APPLICATION
New Plastered Surface: It can be applied over bricks new plastered surface after final trowelling.
Concrete Surface: It can be applied over roof , balcony, podium to make the surface waterproofed.
Over Old Surface: Before application over old plaster surface, the surface is to be vigorously cleaned by wire brush so that it becomes free from oil, dust, grease, algae and any foreign materials. Over the cleaned dry surface Hind Seal Cote is to be applied by brush/spraying after slightly agitating the mixture in the container. It is recommended to recoat the surface where it is porous and penetration even takes place after the first coat. The drying time of Hind Seal Cote depends on the nature of the surface. If the surface is new and fresh it gets dried up within 2-3 hours. For old concrete drying time may get extended due to surface conditions.
PROPERTIES
| Aspect | Transparent Liquid | |
| pH | 10.00 + 2 | |
| Specific gravity | 1.20 + 0.05 at 270 C. | |
| Coverage | Fresh Surface (By Brush/Spray) | 20 -25 Sq. Mtr per Kg |
| Old Surface (By Brush/Spray) | 15-20 Sq. Mtr per Kg |
Note: Coverage may vary depending on the porosity of the surface
APPLICATION TEMPERATURE
Hind Seal Cote is recommended to be applied when the temperature of substrate should not be less than
20 C and higher than 500 C.
SHELF LIFE
12 months from the date of manufacture in unopened condition. To be stored in a cool and dry place away from direct sunlight. It should not be allowed to freeze.
PACKING
20 Kg, 50Kg & 250 Kg Container.
HANDLING PRECAUTIONS
Hind Seal Cote is non-toxic, non-combustible and inhalation to be avoided. Any splashes to skin if happens, wash with water. If contact with eyes occurs, immediately wash with water and seek medical advice.
Hind Tile Cote
EXTERIOR AND INTERIOR SURFACE COATING BASED ON ORGANIC COMPOUND
Hind Tile Cote is an active organic compound based coating and can be applied to any exterior and interior substrate by brush/spray. It is a ready -to-use compound containing active chemicals which when cured forms a hard resilient transparent scratch proof coating on the substrate it is applied.
Technical Data Sheet (TDS)
Product Description
USES
Hind Tile Cote is used as a coating on Ceramic & Vitrified Tiles, Mosaic and Marble surfaces, laid vertically or on floors to give it a protection from scratches, resistant to weathering action and a long lasting protection of the aesthetic look of the surface.
ADVANTAGES
- 1. It provides a tough abrasion resistant surface which does not turn yellow.
- 2. Single component, ready to use.
- 3. Scratch and peel proof.
- 4. It is cost effective due to high coverage.
APPLICATION
Before application the surface is to be vigorously cleaned by water and coir-brushing, so that it becomes free from oil, dust, grease, algae and any foreign materials. Over the cleaned dry surface Hind Tile Cote is to be applied by brush/spraying after slightly agitating the mixture in the container. It is recommended to recoat the surface after the first coat, in opposite direction to overcome any left out portion after first coat application. The drying time of Hind Tile Cote depends on the ambient temperature. Usually it gets completely dry after 4-5 hours of application at 270 C 20 C.
PROPERTIES
| Aspect | Milky Liquid turns transparent when cured. |
| Specific gravity | 1.00 0.05 at 270 C. |
| Coverage | 25 -30 Sq. Mtr per Kg in 2 Coats. |
Note: Coverage may vary depending on the porosity of the surface
APPLICATION TEMPERATURE
Hind Seal Cote is recommended to be applied when the temperature of substrate should not be less than 20 C and higher than 500 C.
SHELF LIFE
12 months from the date of manufacture in unopened condition. To be stored in a cool and dry place away from direct sunlight. It should not be allowed to freeze.
PACKING
20 Kg & 200 Kg Container.
HANDLING PRECAUTIONS
Hind Tile Cote is non-toxic, non-combustible and inhalation to be avoided. Any splashes to skin if happens, wash with water. If contact with eyes occurs, immediately wash with water and seek medical advice.